ExxonMobil Exceed™ 1018EB Metallocene Polyethylene Resin (European Grade)

Category Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer Exxon Chemical
Trade Name Exceed™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Exceed™ 1018EB Metallocene Polyethylene Resin (European Grade).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Exceed 1018EB is a metallocene ethylene-hexene copolymers. Films are made of Exceed 1018EB have outstanding tensile, impact, puncture resistance and low temperature properties. Exceed 1018EB contains slip agent and antiblock, which makes it suitable for formulations which require good openability and a low friction coefficient. It is a ready-to-use versatile polymer for demanding mono layer and multi layer blown film applications.Availability: Africa & Middle East and EuropeAdditive:Antiblock: 2500 ppmSlip: 750 ppm Processing Aid: YesThermal Stabilizer: YesApplications:Agricultural FilmBag in a BoxBarrier Food Packaging Blown FilmBread Bags Food packagingForm Fill and Seal PackagingFreezer FilmGeneral PackagingHeavy Duty BagsLamination FilmMultilayer Packaging FilmOverwrap FilmPackaging FilmsPremium Trash BagsStand Up PouchesTrash Bags Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.918 g/cc
0.0332 lb/in³
ExxonMobil method
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 2500 ppm
2500 ppm
Slip Level 750 ppm
750 ppm
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 440 %
440 %
ASTM D882
Film Elongation at Break, TD 510 %
510 %
ASTM D882
Elmendorf Tear Strength MD 230 g
230 g
ASTM D1922
Elmendorf Tear Strength TD 380 g
380 g
ASTM D1922
Dart Drop Test 750 g
1.65 lb
ASTM D1709
Film Tensile Strength at Break, MD 50.3 MPa
7300 psi
ASTM D882
Film Tensile Strength at Break, TD 35.2 MPa
5100 psi
ASTM D882
1% Secant Modulus, MD 179 MPa
26000 psi
ASTM D882
1% Secant Modulus, TD 179 MPa
26000 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 244 °C
<= 471 °F
Peak Melting Point; ExxonMobil method
Optical Properties Metric English Comments
Haze 4.0 %
4.0 %
ASTM D1003
Gloss 13 %
13 %
45°; ASTM D2457
Descriptive Properties Value Comments
Puncture Force 17 lbf
ExxonMobil Method