ExxonMobil Escorene® LL-3003 LLDPE/Hexene Premium Cast Stretch Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE)/Hexene, Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LL-3003 LLDPE/Hexene Premium Cast Stretch Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A hexene copolymer LLDPE cast film resin. Films made from LL-3003 have outstanding tensile properties as well as stiffness and toughness.Applications: Stretch wrap film; Premium packing film. Data for film properties below based on 0.8 mil film.
Physical Properties Metric English Comments
Density 0.9175 g/cc
0.03315 lb/in³
Exxon Method
Thickness 20.3 microns
0.800 mil
Melt Flow 3.2 g/10 min
3.2 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.00 MPa
1160 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.00 MPa
1160 psi
ASTM D882
Film Elongation at Break, MD 430 %
430 %
ASTM D882
Film Elongation at Break, TD 800 %
800 %
ASTM D882
Secant Modulus, MD 0.131 GPa
19.0 ksi
ASTM D882
Secant Modulus, TD 0.159 GPa
23.1 ksi
ASTM D882
Elmendorf Tear Strength MD 180 g
180 g
ASTM D1922
Elmendorf Tear Strength TD 770 g
770 g
ASTM D1922
Elmendorf Tear Strength, MD 8.86 g/micron
225 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 37.9 g/micron
963 g/mil
ASTM D1922
Dart Drop 3.70 g/micron
94.0 g/mil
F50; ASTM D1709
Dart Drop Test 75.0 g
0.165 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 61.0 MPa
8850 psi
ASTM D882
Film Tensile Strength at Break, TD 34.0 MPa
4930 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 124 °C
255 °F
Exxon Method
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
ASTM D1003
Gloss 96 %
96 %
45°, ASTM D-2457