ExxonMobil Escorene® LD 768.MJ Molding, extrusion and compounding resin

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Extrusion/Coating Grade
Manufacturer	Exxon Chemical
Trade Name	Escorene®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene® LD 768.MJ Molding, extrusion and compounding resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Escorene Ultra LD 768.MJ is a high viscosity, 26.2% vinyl acetate copolymer suitable for making very soft, blow molded or extruded articles with very good low temperature toughness. It can also be used as a polymer modifier to make specialty compounds.Availability: Latin America, North America and South America Additive: Thermal Stabilizer: Yes Applications:CompoundingBlow MoldingViscosity ModifierInformation provided by ExxonMobil Chemical

Physical Properties	Metric	English	Comments
Density	0.951 g/cc	0.0344 lb/in³	ExxonMobil Method
Vinyl Acetate Content	26.2 %	26.2 %	ExxonMobil Method
Melt Flow	2.30 g/10 min @Load 2.16 kg, Temperature 190 °C	2.30 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	75	75	15s; ASTM D2240
Hardness, Shore D	28	28	15s; ASTM D2240
Tensile Strength at Break	9.65 MPa	1400 psi	ASTM D638
Elongation at Break	>= 800 %	>= 800 %	ASTM D638
Flexural Modulus	0.0310 GPa	4.50 ksi	1% secant; ASTM D790
Impact Test	21.7 J @Temperature 23.0 °C	16.0 ft-lb @Temperature 73.4 °F	Instrument Impact, Total Energy; ASTM D3763
	31.2 J @Temperature -40.0 °C	23.0 ft-lb @Temperature -40.0 °F	Instrumented Impact, Total Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	75.0 °C	167 °F	Peak Melting Temperature; ExxonMobil Method
Vicat Softening Point	48.9 °C	120 °F	ASTM D1525

Descriptive Properties	Value	Comments
Features	Thermal Stabilizer

Users viewing this material also viewed the following: