ExxonMobil Escorene® LD-713 High EVA Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-713 High EVA Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 15% vinyl acetate copolymer film resin. Film made from LD-713 exhibits very high impact strength, high clarity and excellent heat sealability.Applications: Meat packaging; Coextruded heat seal layer in food packaging film. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.933 g/cc
0.0337 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 3.5 g/10 min
3.5 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 4.00 MPa
580 psi
ASTM D882
Film Tensile Strength at Yield, TD 3.00 MPa
435 psi
ASTM D882
Film Elongation at Break, MD 190 %
190 %
ASTM D882
Film Elongation at Break, TD 650 %
650 %
ASTM D882
Secant Modulus, MD 0.0700 GPa
10.2 ksi
ASTM D882
Secant Modulus, TD 0.0800 GPa
11.6 ksi
ASTM D882
Elmendorf Tear Strength MD 60 g
60 g
ASTM D1922
Elmendorf Tear Strength TD 50 g
50 g
ASTM D1922
Elmendorf Tear Strength, MD 1.89 g/micron
48.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 1.57 g/micron
40.0 g/mil
ASTM D1922
Dart Drop 9.45 g/micron
240 g/mil
F50; ASTM D1709
Dart Drop Test 300 g
0.662 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 29.0 MPa
4210 psi
ASTM D882
Film Tensile Strength at Break, TD 24.0 MPa
3480 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 87.0 °C
189 °F
Exxon Method
Optical Properties Metric English Comments
Haze 3.0 %
3.0 %
ASTM D1003
Gloss 80 %
80 %
45°, ASTM D-2457