ExxonMobil Escorene™ LD 708.62 Ethylene Vinyl Acetate Copolymer

Category	Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer	Exxon Chemical
Trade Name	Escorene™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escorene™ LD 708.62 Ethylene Vinyl Acetate Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Escorene Ultra UL 708.62 is a 14.9% VA copolymer film resin. Film made from LD 708.62 exhibits good impact strength and superior heat sealabilty.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications:Cheese PackagingMeat PackagingPrimal Meat BagsInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.935 g/cc	0.0338 lb/in³	ExxonMobil method
Vinyl Acetate Content	14.9 %	14.9 %	ExxonMobil method
Melt Flow	5.2 g/10 min @Load 2.16 kg, Temperature 190 °C	5.2 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	320 %	320 %	ASTM D882
Film Elongation at Break, TD	870 %	870 %	ASTM D882
Elmendorf Tear Strength MD	210 g	210 g	ASTM D1922
Elmendorf Tear Strength TD	220 g	220 g	ASTM D1922
Dart Drop Test	100 g	0.221 lb	ASTM D1709A
Film Tensile Strength at Break, MD	29.6 MPa	4300 psi	ASTM D882
Film Tensile Strength at Break, TD	19.3 MPa	2800 psi	ASTM D882
1% Secant Modulus, MD	75.8 MPa	11000 psi	ASTM D882
1% Secant Modulus, TD	82.7 MPa	12000 psi	ASTM D882

Thermal Properties	Metric	English	Comments
Melting Point	<= 190 °C	<= 374 °F	Peak Melting Point; ExxonMobil method
Vicat Softening Point	62.8 °C	145 °F	ASTM D1525

Optical Properties	Metric	English	Comments
Haze	1.1 %	1.1 %	ASTM D1003
Gloss	86 %	86 %	45°; ASTM D2457