ExxonMobil Escorene™ LD 705.MJ Blown Ethylene Vinyl Acetate Copolymer

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ LD 705.MJ Blown Ethylene Vinyl Acetate Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Escorene Ultra LD 705.MJ is a fractional melt index, 12.8 wt% vinyl acetate copolymer specialty film resin for applications requiring outstanding heat sealability, strength, and toughness.Availability: Latin America, North America and South AmericaAdditive:Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications: CompoundingFreezer FilmHeat Seal LayerLiquid PackagingPrimal Meat BagsProfile ExtrusionStretch FilmInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.935 g/cc
0.0338 lb/in³
ExxonMobil method
Vinyl Acetate Content 12.8 %
12.8 %
ExxonMobil method
Melt Flow 0.40 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.40 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 77

@Time 15.0 sec
77

@Time 0.00417 hour
ASTM D2240
Hardness, Shore D 39

@Time 15.0 sec
39

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break 15.9 MPa
2300 psi
ASTM D638
Tensile Strength, Yield 6.34 MPa
920 psi
ASTM D638
Elongation at Break >= 800 %
>= 800 %
ASTM D638
Elongation at Yield 180 %
180 %
ASTM D638
Flexural Modulus, 1% Secant 89.6 MPa
13000 psi
ASTM D790
Dart Drop, Total Energy 19.0 J

@Temperature 22.8 °C
14.0 ft-lb

@Temperature 73.0 °F
ASTM D3763
32.5 J

@Temperature -40.0 °C
24.0 ft-lb

@Temperature -40.0 °F
ASTM D3763
Thermal Properties Metric English Comments
Melting Point <= 201 °C
<= 394 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 77.2 °C
171 °F
ASTM D1525