ExxonMobil Escorene® LD-336 EVA Film Resin, Clarity, Very High Drawdown  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-336 EVA Film Resin, Clarity, Very High Drawdown  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 3.5% vinyl acetate copolymer blown film resin capable of very high drawdown with excellent clarity.Applications: Very thin heat seal layers; Light weight bags. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 6.5 g/10 min
6.5 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 5.00 MPa
725 psi
ASTM D882
Film Tensile Strength at Yield, TD 4.90 MPa
711 psi
ASTM D882
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 550 %
550 %
ASTM D882
Secant Modulus, MD 0.110 GPa
16.0 ksi
ASTM D882
Secant Modulus, TD 0.117 GPa
17.0 ksi
ASTM D882
Elmendorf Tear Strength MD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength, MD 4.72 g/micron
120 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 4.72 g/micron
120 g/mil
ASTM D1922
Dart Drop 2.36 g/micron
60.0 g/mil
F50; ASTM D1709
Dart Drop Test 75.0 g
0.165 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 23.0 MPa
3340 psi
ASTM D882
Film Tensile Strength at Break, TD 15.0 MPa
2180 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 105 °C
221 °F
Exxon Method
Optical Properties Metric English Comments
Haze 2.6 %
2.6 %
ASTM D1003
Gloss 86 %
86 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified