ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-333 exhibits superior impact strength, clarity and heat sealability.Applications: Primal meat bags; Retail meat packages; Cheese packaging. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 0.90 g/10 min
0.90 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 7.60 MPa
1100 psi
ASTM D882
Film Tensile Strength at Yield, TD 6.20 MPa
899 psi
ASTM D882
Film Elongation at Break, MD 230 %
230 %
ASTM D882
Film Elongation at Break, TD 635 %
635 %
ASTM D882
Secant Modulus, MD 0.130 GPa
18.9 ksi
ASTM D882
Secant Modulus, TD 0.160 GPa
23.2 ksi
ASTM D882
Elmendorf Tear Strength MD 110 g
110 g
ASTM D1922
Elmendorf Tear Strength TD 70 g
70 g
ASTM D1922
Elmendorf Tear Strength, MD 3.46 g/micron
88.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.20 g/micron
56.0 g/mil
ASTM D1922
Dart Drop 7.87 g/micron
200 g/mil
F50; ASTM D1709
Dart Drop Test 250 g
0.551 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 37.0 MPa
5370 psi
ASTM D882
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 99.0 °C
210 °F
Exxon Method
Optical Properties Metric English Comments
Haze 3.0 %
3.0 %
ASTM D1003
Gloss 77 %
77 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified