ExxonMobil Escorene® LD-306 EVA Film Resin, High Clarity, Very High Impact  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Vinyl Acetate , Ethylene Vinyl Acetate Copolymer (EVA), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-306 EVA Film Resin, High Clarity, Very High Impact  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A 5.5% vinyl acetate copolymer, high clarity film resin. Film made from this resin exhibits superior impact strength and heat sealability.Applications: Frozen food packaging; Other food packaging such as heavy duty produce bags, rice bags, poultry bags, etc.; Applications requiring excellent toughness and good heat sealability. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.926 g/cc
0.0335 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 8.30 MPa
1200 psi
ASTM D882
Film Tensile Strength at Yield, TD 6.90 MPa
1000 psi
ASTM D882
Film Elongation at Break, MD 150 %
150 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.130 GPa
18.9 ksi
ASTM D882
Secant Modulus, TD 0.160 GPa
23.2 ksi
ASTM D882
Elmendorf Tear Strength MD 350 g
350 g
ASTM D1922
Elmendorf Tear Strength TD 100 g
100 g
ASTM D1922
Elmendorf Tear Strength, MD 11.0 g/micron
280 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.15 g/micron
80.0 g/mil
ASTM D1922
Dart Drop 3.15 g/micron
80.0 g/mil
F50; ASTM D1709
Dart Drop Test 100 g
0.221 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 30.0 MPa
4350 psi
ASTM D882
Film Tensile Strength at Break, TD 19.0 MPa
2760 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 103 °C
217 °F
Exxon Method
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
ASTM D1003
Gloss 65 %
65 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified