ExxonMobil Escorene® LD-140 LDPE Industrial Film resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-140 LDPE Industrial Film resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A fractional melt index homopolymer resin for production of film with very good toughness.Applications: Heavy duty bags. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.921 g/cc
0.0333 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 0.75 g/10 min
0.75 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 12.0 MPa
1740 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 120 %
120 %
ASTM D882
Film Elongation at Break, TD 600 %
600 %
ASTM D882
Secant Modulus, MD 0.230 GPa
33.4 ksi
ASTM D882
Secant Modulus, TD 0.320 GPa
46.4 ksi
ASTM D882
Elmendorf Tear Strength MD 450 g
450 g
ASTM D1922
Elmendorf Tear Strength TD 80 g
80 g
ASTM D1922
Elmendorf Tear Strength, MD 14.2 g/micron
360 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 2.52 g/micron
64.0 g/mil
ASTM D1922
Dart Drop 2.52 g/micron
64.0 g/mil
F50; ASTM D1709
Dart Drop Test 80.0 g
0.176 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 35.0 MPa
5080 psi
ASTM D882
Film Tensile Strength at Break, TD 21.0 MPa
3050 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 108 °C
226 °F
Exxon Method
Optical Properties Metric English Comments
Haze 14 %
14 %
ASTM D1003
Gloss 45 %
45 %
45°, ASTM D-2457