ExxonMobil Escorene® LD-117 MDPE Blown Overwrap Film Resin, Tough  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-117 MDPE Blown Overwrap Film Resin, Tough  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A homopolymer film resin with good clarity and excellent stiffness. Film made from LD-117 can be used in overwrap applications and in push-through type packaging equipment. Film produced from LD-117 can be drawn down to 1.0 mil gauge.Applications: Bakery product overwrap; Soft goods (paper products) overwrap; Film is particularly suitable for applications requiring stiffness, crispness, machinability and abrasion resistance. Data for film properties below based on 1.5 mil film.
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
Exxon Method
Thickness 38.1 microns
1.50 mil
Melt Flow 1.6 g/10 min
1.6 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.0 MPa
1890 psi
ASTM D882
Film Tensile Strength at Yield, TD 15.0 MPa
2180 psi
ASTM D882
Film Elongation at Break, MD 150 %
150 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Secant Modulus, MD 0.280 GPa
40.6 ksi
ASTM D882
Secant Modulus, TD 0.320 GPa
46.4 ksi
ASTM D882
Elmendorf Tear Strength MD 125 g
125 g
ASTM D1922
Elmendorf Tear Strength TD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength, MD 3.27 g/micron
83.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.94 g/micron
100 g/mil
ASTM D1922
Dart Drop 1.57 g/micron
40.0 g/mil
F50; ASTM D1709
Dart Drop Test 60.0 g
0.132 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 27.0 MPa
3920 psi
ASTM D882
Film Tensile Strength at Break, TD 17.0 MPa
2470 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 116 °C
241 °F
Exxon Method
Optical Properties Metric English Comments
Haze 7.0 %
7.0 %
ASTM D1003
Gloss 65 %
65 %
45°, ASTM D-2457