ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® LD-104 LDPE Packaging Film Resin, High Clarity  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A homopolymer packaging film resin with excellent clarity and good stiffness. It is excellent either blown film or chill roll casting equipment. In blown film equipment LD-104 can be drawn down to 1.0 mil gauge.Applications: Food packaging (sandwich bags, baked goods bags, light duty produce bags, etc.); Textile goods packaging (shirts, sweaters, etc.); Other packaging applications requiring excellent clarity film. Data for film properties below based on 1.25 mil film.
Physical Properties Metric English Comments
Density 0.925 g/cc
0.0334 lb/in³
Exxon Method
Thickness 31.8 microns
1.25 mil
Melt Flow 2.0 g/10 min
2.0 g/10 min
Exxon Method
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.70 MPa
1410 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 500 %
500 %
ASTM D882
Secant Modulus, MD 0.210 GPa
30.5 ksi
ASTM D882
Secant Modulus, TD 0.250 GPa
36.3 ksi
ASTM D882
Elmendorf Tear Strength MD 150 g
150 g
ASTM D1922
Elmendorf Tear Strength TD 350 g
350 g
ASTM D1922
Elmendorf Tear Strength, MD 4.72 g/micron
120 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 11.0 g/micron
280 g/mil
ASTM D1922
Dart Drop 2.20 g/micron
56.0 g/mil
F50; ASTM D1709
Dart Drop Test 70.0 g
0.154 lb
F50; ASTM D-1709
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ASTM D882
Film Tensile Strength at Break, TD 18.0 MPa
2610 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 113 °C
235 °F
Exxon Method
Optical Properties Metric English Comments
Haze 5.0 %
5.0 %
ASTM D1003
Gloss 70 %
70 %
45°, ASTM D-2457
Transmission, Visible 90 %
90 %
clear; thickness not quantified