ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets (discontinued **)
| Category | Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Rotational Molding Grade |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Escorene® HD-8660 HDPE, Rotational Molding Pellets
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data Provided by Exxon Chemical Canada.Characteristics: Fully formulated UV-8 type protection, Higher stiffness & impact strengthUses: Large agricultural tanks, Industrial products
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in³ | ASTM D4883 |
| Environmental Stress Crack Resistance | 200 hour | 200 hour | F-50; 10% Igepal Cond. B; ASTM D-1693 |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 18.6 MPa | 2700 psi | ASTM D638 |
| Elongation at Break | 350 % | 350 % | ASTM D638 |
| Flexural Modulus | 0.710 GPa | 103 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 133 °C | 271 °F | Exxon Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 54.0 °C | 129 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 42.0 °C | 108 °F | ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRICOMP DFL36ELH PC (Asia Pacific)
- Overview of materials for High Density Polyethylene (HDPE), Film Grade
- Fiberfil® PP-62/MI/25 Polypropylene Copolymer, 25% Mica Reinforced
- Magyar Aluminum ALOLT 21AF Aluminum Hydroxide
- A. Schulman POLYBATCH™ Light Blue 40442 Concentrate Based In LLDPE
- A. Schulman POLYFORT™ FPP 3717 Talc Filled Homopolymer Polypropylene (39.6% Mineral Content)
- Tipco Tipcolene® FPT 40 NEX - 40% Talc Reinforced Polypropylene Homopolymer, Low MFI
- A. Schulman SCHULADUR® A GB20 20% Glass Bead Reinforced PBT
- 3M 8440 Silicone Rubber Cold Shrink Connector Insulators
- Sinotek Materials MD-3 Graphite Emulsion
Copyright © lookpolymers.com All Rights Reserved