ExxonMobil Escorene® HD-7756 HMW-HDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® HD-7756 HMW-HDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A high molecular weight HDPE blown film resin. Films made from HD-7756 exhibit excellent impact and toughness properties as well as high stiffness. HD-7756 is particularly recommended for films less than 0.5 mil in thickness.Applications: Retail carry-out sacks; Merchandise bags; Institutional can liners; Consumer trash bags. Data for film properties below based on 0.5 mil film.
Physical Properties Metric English Comments
Density 0.9535 g/cc
0.03445 lb/in³
Exxon Method
Thickness 12.7 microns
0.500 mil
Melt Flow 0.055 g/10 min
0.055 g/10 min
Exxon Method (I2). HLMI (I21) is 9 g/10 min.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 42.0 MPa
6090 psi
ASTM D882
Film Tensile Strength at Yield, TD 34.0 MPa
4930 psi
ASTM D882
Film Elongation at Break, MD 270 %
270 %
ASTM D882
Film Elongation at Break, TD 430 %
430 %
ASTM D882
Secant Modulus, MD 1.285 GPa
186.4 ksi
ASTM D882
Secant Modulus, TD 1.415 GPa
205.2 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.394 g/micron
10.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.51 g/micron
140 g/mil
ASTM D1922
Dart Drop 16.9 g/micron
430 g/mil
F50; ASTM D-1709
Film Tensile Strength at Break, MD 95.0 MPa
13800 psi
ASTM D882
Film Tensile Strength at Break, TD 66.0 MPa
9570 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 129 °C
264 °F
Exxon Method