ExxonMobil Escorene® HD-7000F HMW-HDPE Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene® HD-7000F HMW-HDPE Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, Exxon Chemical.A high molecular weight HDPE blown film resin. Films made from HD-7000F exhibit excellent impact and toughness properties as well as high stiffness. HD-7000F is particularly recommended for films 0.5 mil or greater in thickness.Applications: Retail carry-out sacks; Merchandise bags; Institutional can liners; Consumer trash bags. Data for film properties below based on 0.5 mil film.
Physical Properties Metric English Comments
Density 0.952 g/cc
0.0344 lb/in³
Exxon Method
Thickness 12.7 microns
0.500 mil
Melt Flow 0.045 g/10 min
0.045 g/10 min
Exxon Method (I2). HLMI (I21) is 8 g/10 min.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 39.0 MPa
5660 psi
ASTM D882
Film Tensile Strength at Yield, TD 33.0 MPa
4790 psi
ASTM D882
Film Elongation at Break, MD 300 %
300 %
ASTM D882
Film Elongation at Break, TD 400 %
400 %
ASTM D882
Secant Modulus, MD 0.965 GPa
140 ksi
ASTM D882
Secant Modulus, TD 1.14 GPa
165 ksi
ASTM D882
Elmendorf Tear Strength, MD 0.591 g/micron
15.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 3.15 g/micron
80.0 g/mil
ASTM D1922
Dart Drop 24.6 g/micron
625 g/mil
F50; ASTM D-1709
Film Tensile Strength at Break, MD 93.0 MPa
13500 psi
ASTM D882
Film Tensile Strength at Break, TD 72.0 MPa
10400 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 129 °C
264 °F
Exxon Method
Copyright © lookpolymers.com All Rights Reserved