ExxonMobil Escorene™ 768.MJ Blown Ethylene Vinyl Acetate Copolymer

Category Polymer , Thermoplastic , Ethylene Vinyl Acetate
Manufacturer Exxon Chemical
Trade Name Escorene™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escorene™ 768.MJ Blown Ethylene Vinyl Acetate Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Escorene Ultra UL 768.MJ is a low gel 26.2% vinyl acetate copolymer designed for film and compounding applications. This resin provides very low modulus films with high tensile strength and impact strength.Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: NoThermal Stabilizer: Yes Applications:CompoundingBatch Inclusion BagsElastic FilmsHigh Frequency SealingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.951 g/cc
0.0344 lb/in³
ExxonMobil method
Vinyl Acetate Content 26.2 %
26.2 %
ExxonMobil method
Melt Flow 2.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 450 %
450 %
ASTM D882
Film Elongation at Break, TD 730 %
730 %
ASTM D882
Elmendorf Tear Strength MD 40 g
40 g
ASTM D1922
Elmendorf Tear Strength TD 460 g
460 g
ASTM D1922
Dart Drop Test 460 g
1.01 lb
ASTM D1709A
Film Tensile Strength at Break, MD 35.2 MPa
5100 psi
ASTM D882
Film Tensile Strength at Break, TD 34.5 MPa
5000 psi
ASTM D882
1% Secant Modulus, MD 29.0 MPa
4200 psi
ASTM D882
1% Secant Modulus, TD 31.0 MPa
4500 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point <= 165 °C
<= 329 °F
Peak Melting Point; ExxonMobil method
Vicat Softening Point 47.8 °C
118 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 2.1 %
2.1 %
ASTM D1003
Gloss 80 %
80 %
45°; ASTM D2457