ExxonMobil Escor® AT-310 EMAAA Terpolymer for Polymer Modification (discontinued **)

Category	Polymer , Thermoplastic , EMAAA Terpolymer , Ethylene Methyl Acrylate
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Escor® AT-310 EMAAA Terpolymer for Polymer Modification (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by the manufacturer, Exxon Chemical.45 Acid Number. Provides unusual adhesion to a variety of substrates and other components such as aluminum foil, polyolefins, polycarbonate, PET, etc.Applications: High end-use temperature adhesive; Engineering thermoplastic modifier; Heat activated sealant; Adhesion of dissimilar materials such as elastomers to metals.

Physical Properties	Metric	English	Comments
Density	0.941 g/cc	0.0340 lb/in³	Exxon Method
Melt Flow	6.0 g/10 min	6.0 g/10 min	Exxon Method

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	90	90	ASTM D2240
Hardness, Shore D	41	41	ASTM D2240
Tensile Strength, Ultimate	14.0 MPa	2030 psi	ASTM D638
Tensile Strength, Yield	3.30 MPa	479 psi	ASTM D638
Elongation at Break	570 %	570 %	ASTM D638
Modulus of Elasticity	0.0190 GPa	2.76 ksi	ASTM D638
Flexural Modulus	0.0600 GPa	8.70 ksi	ASTM D790
Tensile Impact Strength	530 kJ/m²	252 ft-lb/in²	23°C; ASTM D-1822

Thermal Properties	Metric	English	Comments
Melting Point	94.0 °C	201 °F	Exxon Method
Vicat Softening Point	66.0 °C	151 °F	1000g; ASTM D-1525
Glass Transition Temp, Tg	74.0 °C	165 °F	DSC