ExxonMobil Escor™ 5100 ExCo Ethylene Acrylic Acid Copolymer Resin

Category Polymer , Thermoplastic , Ethylene Acrylic Acid
Manufacturer Exxon Chemical
Trade Name Escor™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Escor™ 5100 ExCo Ethylene Acrylic Acid Copolymer Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Escor 5100 is primarily intended for extrusion coating, coextrusion coating and extrusion lamination. Excellent adhesion to polar substrates, aluminum foil, metalized films, papers, iron, steel and glass. High bond resistance also when used to pack acidic food products. Excellent coextrusion adhesive resin for Polyamides. Outstanding sealing performance: very low temperature sealing with high seal strengths, high hot tack forces and good seal through contamination. Very good adhesive polymer in film.Availability: Africa & Middle East, Asia Pacific and Europe Additive: Antiblock: NoSlip: No Thermal Stabilizer: NoApplications:Aluminum Containing PackagingCable ShieldingCoextrusion Coating Extrusion CoatingExtrusion LaminationFood packaging Metalized Films Information provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.940 g/cc
0.0340 lb/in³
ExxonMobil method
Acrylic Acid Content 11 %
11 %
ExxonMobil Method
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Neck In 10.9 cm

@Temperature 280 °C
4.30 in

@Temperature 536 °F
328 ft/min, constant output at 35 rpm; ExxonMobil Method
16.8 cm

@Temperature 280 °C
6.60 in

@Temperature 536 °F
164 ft/min, constant output at 35 rpm; ExxonMobil Method
Drawdown 4.00 m/s

@Temperature 280 °C
787 ft/min

@Temperature 536 °F
Constant output at 35 rpm; ExxonMobil Method
Thermal Properties Metric English Comments
Melting Point <= 203 °C
<= 397 °F
Peak Melting Point; ExxonMobil method