- ExxonMobil EXACT™ 4053 Plastomer for Film Applications
ExxonMobil EXACT™ 4053 Plastomer for Film Applications
| Category | Polymer , Film , Thermoplastic , Elastomer, TPE , Thermoplastic Olefinic Elastomer (TPO), Film Grade , Polyethylene (PE) |
| Manufacturer | Exxon Chemical |
| Trade Name | EXACT™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil EXACT™ 4053 Plastomer for Film Applications.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Exact 4053 is an ethylene-based butene plastomer produced using ExxonMobil Chemical’s EXXPOL® Catalyst Technology. This resin is designed primarily for use in blends with polyolefines to improve the heat sealing performance and/or toughness in film applications. Exact 4053 contains no antioxidants. Availability: Latin America, North America and South America Additive: Antiblock: NoSlip: No Thermal Stabilizer: NoApplications:Blend PartnerBlown Film Data provided by the manufacturer, Exxon Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.888 g/cc | 0.0321 lb/in³ | Exxon Method |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 3.52 MPa | 511 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 3.10 MPa | 450 psi | ASTM D882 |
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 |
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 |
| Film Elongation at Yield, MD | 10 % | 10 % | ASTM D882 |
| Film Elongation at Yield, TD | 10 % | 10 % | ASTM D882 |
| Secant Modulus, MD | 0.0669 GPa | 9.70 ksi | ASTM D882 |
| Secant Modulus, TD | 0.0758 GPa | 11.0 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 1.97 g/micron | 50.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 5.12 g/micron | 130 g/mil | ASTM D1922 |
| Dart Drop | 5.51 g/micron | 140 g/mil | ASTM D-1709 |
| Film Tensile Strength at Break, MD | 57.2 MPa | 8300 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 49.6 MPa | 7190 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 70.0 °C | 158 °F | Peak Melting, Exxon Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.6 % | 1.6 % | ASTM D1003 |
| Gloss | 85 % | 85 % | 45; ASTM D-2457 |