ExxonMobil ESCOR™ AT 310 Blown Film Resin  (discontinued **)

Category Polymer , Film , Thermoplastic , Ethylene Acrylic Acid , Ethylene Methyl Acrylate
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil ESCOR™ AT 310 Blown Film Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ESCOR AT 310 is an acid terpolymer which provides excellent adhesion to a variety of polar and non-polar materials such as metals, glass, polyolefins, polyamides, polyesters, etc. It is suitable for use as a polymer modifier to improve adhesion.Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Methyl Acrylate Content 6.5 %
6.5 %
Acrylic Acid Content 6.5 %
6.5 %
Melt Flow 6.0 g/10 min
6.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 370 %
370 %
ASTM D882
Film Elongation at Break, TD 570 %
570 %
ASTM D882
Elmendorf Tear Strength, MD 5.51 g/micron
140 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 13.0 g/micron
330 g/mil
ASTM D1922
Dart Drop 11.8 g/micron
300 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 29.2 MPa
4240 psi
ASTM D882
Film Tensile Strength at Break, TD 28.1 MPa
4080 psi
ASTM D882
1% Secant Modulus, MD 67.6 MPa
9810 psi
ASTM D882
1% Secant Modulus, TD 66.5 MPa
9640 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 87.2 °C
189 °F
Peak Melting Temperature; ExxonMobil Method
Descriptive Properties Value Comments
Features Thermal Stabilizer