ExxonMobil Bicor® 70 HSH OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 70 HSH OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor HSH is a one-side treated, one-side sealable, coextruded OPP film designed for use in unsupported plain or surface print high-speed horizontal applications.Availability: Latin America, North America and South AmericaKey Features:Excellent opticsExcellent hot slip properties for high-speed applicationsLow MST, broad seal range layerNon-migratory slip system for consistent COFFeatures:In Lamination Lap SealableApplications:BakeryBiscuts/Cookie/Crackers Confectionery, GumConfectionery, SugarCrips and Snacks Uses:HFFS Flexible Packaging Processing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 7.10 g/m²/day | 0.457 g/100 in²/day | 38°C, 90% RH; ExxonMobil Method |
| Thickness | 17.8 microns | 0.700 mil | Nominal; ExxonMobil Method |
| Coating Weight | 15.7 g/m² | 9.80 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.40 | 0.40 | Untreated; ExxonMobil Method |
| 0.40 | 0.40 | Treated; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 124 MPa | 18000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 248 MPa | 36000 psi | 20 in/min, 2.0 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Shrinkage, TD | 4.5 % | 4.5 % | at 275°F; ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.9 % | 1.9 % | ExxonMobil Method |
| Gloss | 90 % | 90 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST, | 195°F | |
| Crimp Seal Strength | 450 g/in | 240°F, 20psi, 3/4sec |
| Wetting Tension | 0.88 receding COS theta | Treated Surface |
| Yield | 44000 in2/lb |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable JLK51A Polyvinyl Chloride, Flexible (PVC, Flexible)
- PBI Performance Products Celazole® TF-60 C Carbon Fiber Reinforced Melt Processable Polybenzimidazole
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR N650 Filler
- Mikro-Technik DT R Carboxymethylcellulose (CMC)
- A. Schulman POLYFORT™ FPP 1007X Extra High Flow, Talc Fortified Homopolymer Polypropylene
- Arkema Group Lucalor® RB 8067 CPVC, Pipe Grade
- Buckeye Polymers BP RPP 4012 T BLK Polypropylene, Talc Filled
- Teknor Apex Sarlink® 4439D Thermoplastic Elastomer
Copyright © lookpolymers.com All Rights Reserved