Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 60 SLP OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: Bicor SLP is a one-side treated, non-heat sealable OPP film designed for use as the outside web of a lamination. The treated print surface is intended as the print and laminating side.Availability: Latin America, North America and South AmericaKey Features:SLP provides excellent bond strength in adhesive, PVdC adhesive, and extrusion laminations.The treated print surface of SLP is receptive to water-based and solvent-based inks and adhesivesSLP provides exceptional print quality equality and excellent ink adhesionNon-migratory slip system for consistent COFApplications:BakeryBiscuits/Cookie/CrackersConfectionery, GumConfectionery, SugarCrisps and SnacksFresh ProduceUses:HFFS Flexible PackagingPouches – Flexible PackagingVFFS Flexible PackagingProcessing Method: Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Water-based Flexographic PrintingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 8.38 g/m²/day

@Temperature 38.0 °C
0.540 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Thickness 15.2 microns
0.600 mil
ExxonMobil Method
Coating Weight 13.6 g/m²
8.50 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Coefficient of Friction 0.20
0.20
Slip Modified; ExxonMobil Method
Film Tensile Strength at Break, MD 124 MPa
18000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 241 MPa
35000 psi
20 in/min, 2.0 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C
5.0 %

@Temperature 275 °F
ExxonMobil Method
Optical Properties Metric English Comments
Haze 2.0 %
2.0 %
ExxonMobil Method
Gloss 88 %
88 %
45°, Untreated Surface; ExxonMobil Method
Descriptive Properties Value Comments
Wetting Tension 0.83 receding cos theta
Treated Surface
Yield 50700 in2/lb