Material Notes:

Product Description: A is a biaxially oriented transparent polypropylene film, acrylic coated tow sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strength even under low pressureGood aroma barrierExcellent packaging machine performancesOutstanding optical propertiesIdeal support for normal ink systemsWater-based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierIn Lamination Lap SealableApplications:Biscuits/Cookie/CrackersBox OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksHealth and Beauty CareHousehold and Detergents Pet Food Uses: Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	0.807 g/m²/day @Temperature 23.0 °C	0.0520 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.04 g/m²/day @Temperature 38.0 °C	0.260 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	650 cc/m²/day @Temperature 23.0 °C	41.9 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	652 cc/m²/day @Temperature 23.0 °C	42.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	35.6 microns	1.40 mil	ExxonMobil Method
Coating Weight	31.2 g/m²	19.5 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	175 %	175 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	65 %	65 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.50 GPa	508 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Both Sides; ExxonMobil Method
Seal Strength	610 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C	610 g/in @Pressure 40.0 psi, Temperature 266 °F	Otto Bruger, 0.2 sec; ExxonMobil Method
Film Tensile Strength at Break, MD	120 MPa	17400 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	245 MPa	35500 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	4.0 % @Temperature 135 °C, Time 432 sec	4.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	2.0 % @Temperature 135 °C, Time 432 sec	2.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.5 %	1.5 %	ExxonMobil Method
Gloss	85 %	85 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	90°F	36.3 psi, 0.2 sec
Yield	22100 in²/lb