ExxonMobil Bicor™ 30MB666 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 30MB666 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A biaxially oriented transparent polypropylene film, acrylic coated two sides. It provides outstanding performance on all packaging machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Low sealing thresholdHigh seal strengths even under low pressure sealingGood aroma barrierExcellent packaging machine performanceOutstanding optical propertiesIdeal support for normal ink systemsWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma Barrier In Lamination Lap SealableApplications:Biscuits/Cookie/CrackersBox Overwrap Confectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksHealth and Beauty CareHousehold and DetergentsPet Food Uses: Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 1.01 g/m²/day

@Temperature 23.0 °C
0.0650 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
4.50 g/m²/day

@Temperature 38.0 °C
0.290 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 745 cc/m²/day

@Temperature 23.0 °C
48.0 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
751 cc/m²/day

@Temperature 23.0 °C
48.4 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
Thickness 30.5 microns
1.20 mil
ExxonMobil Method
Coating Weight 27.4 g/m²
17.1 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 200 %
200 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 65 %
65 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 2.20 GPa
319 ksi
MD; ExxonMobil Method
3.50 GPa
508 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.25
0.25
Both Sides; ExxonMobil Method
Seal Strength 200 g/25 mm

@Pressure 0.00345 MPa,
Temperature 100 °C
200 g/in

@Pressure 0.500 psi,
Temperature 212 °F
0.5 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 135 MPa
19600 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 275 MPa
39900 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.4 %
1.4 %
ExxonMobil Method
Gloss 85 %
85 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Heat Seal Range 90°F
36.3 psi, 0.2 sec
Yield 25200 in2/lb