| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 30MB400 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: A heat sealable coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 30MB400 can be either used as mono material or in laminated structures.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding optical propertiesGood seal strengthGood dimensional stabilityGood hot slipGood hot tackFeatures: In Lamination Lap SealableApplications:BakeryBiscuits/Cookie/CrackersBox Overwrap Confectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPaper Ream wrapPet Food Uses: HFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.01 g/m²/day @Temperature 23.0 °C |
0.0650 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 4.50 g/m²/day @Temperature 38.0 °C |
0.290 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 30.5 microns | 1.20 mil | ExxonMobil Method |
| Coating Weight | 26.9 g/m² | 16.8 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 205 % | 205 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 55 % | 55 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.50 GPa | 508 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.30 | 0.30 | Both Sides; ExxonMobil Method |
| Seal Strength | 300 g/25 mm @Pressure 0.0689 MPa, Temperature 120 °C |
300 g/in @Pressure 10.0 psi, Temperature 248 °F |
Treated Surface, 0.8 sec; ExxonMobil Method |
| 300 g/25 mm @Pressure 0.0689 MPa, Temperature 115 °C |
300 g/in @Pressure 10.0 psi, Temperature 239 °F |
Untreated Surface, 0.8 sec; ExxonMobil Method | |
| Film Tensile Strength at Break, MD | 140 MPa | 20300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.0 % | 2.0 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 25700 in2/lb |