ExxonMobil Bicor™ 26MB768 OPP Film

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer Exxon Chemical
Trade Name Bicor™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Bicor™ 26MB768 OPP Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A high gas barrier, biaxially oriented transparent polypropylene film, coated on one side PVdC, one side very low temperature seal (VLTS) coating. PVdC provides an excellent moisture, gas and aroma protection for all types of products and VLTS coating provides excellent performance on high speed HFFS machines.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent moisture, oxygen and aroma barriersExceptionally wide sealing range with a low minimum seal temperature (MST)Excellent seal strength and hot tackRobust performance on horizontal flowpack machinesExcellent seal retention in humid conditionsOutstanding optical propertiesWater-based coatingsFeatures: Flavor & Aroma BarrierGas BarrierHigh Barrier Printable PVdC CoatedHumidity ResistantIn Lamination Lap SealableMoisture BarrierOxygen BarrierVery Broad Seal RangeVLTS CoatedApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Chocolate Confectionery, Gum Confectionery, Sugar Health and Beauty Care Uses:HFFS Flexible Packaging Processing Method: Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil
Physical Properties Metric English Comments
Water Vapor Transmission 0.900 g/m²/day

@Temperature 23.0 °C
0.0580 g/100 in²/day

@Temperature 73.4 °F
85% RH; ExxonMobil Method
2.95 g/m²/day

@Temperature 38.0 °C
0.190 g/100 in²/day

@Temperature 100 °F
90% RH; ExxonMobil Method
Oxygen Transmission Rate 20.0 cc/m²/day

@Temperature 23.0 °C
1.29 cc/100 in²/day

@Temperature 73.4 °F
Wet, 75% RH; ExxonMobil Method
20.2 cc/m²/day

@Temperature 23.0 °C
1.30 cc/100 in²/day

@Temperature 73.4 °F
0% RH; ExxonMobil Method
Thickness 25.4 microns
1.00 mil
ExxonMobil Method
Coating Weight 23.5 g/m²
14.7 lb/ream
ExxonMobil Method
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 200 %
200 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD 65 %
65 %
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity 2.20 GPa
319 ksi
MD; ExxonMobil Method
3.50 GPa
508 ksi
TD; ExxonMobil Method
Coefficient of Friction 0.28
0.28
PVdC; ExxonMobil Method
0.40
0.40
VLTS; ExxonMobil Method
Seal Strength 410 g/25 mm

@Pressure 0.138 MPa,
Temperature 80.0 °C
410 g/in

@Pressure 20.0 psi,
Temperature 176 °F
LTS, 0.8 sec; ExxonMobil Method
Film Tensile Strength at Break, MD 135 MPa
19600 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD 275 MPa
39900 psi
7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Thermal Properties Metric English Comments
Shrinkage, MD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Shrinkage, TD 5.0 %

@Temperature 135 °C,
Time 432 sec
5.0 %

@Temperature 275 °F,
Time 0.120 hour
ExxonMobil Method
Optical Properties Metric English Comments
Haze 1.6 %
1.6 %
ExxonMobil Method
Gloss 98 %
98 %
45°; ExxonMobil Method
Descriptive Properties Value Comments
Carbon Dioxide Transmission Rate 5.16 cc/100 in2/ 24 hr
75% RH, ASTM D1434
Heat Seal Range 126°F
36.3 psi, 0.2 sec
Nitrogen Transmission Rate 0.645 cc/100 in2/ 24 hr
75% RH, ASTM D1434
Yield 29300 in2/lb