ExxonMobil Bicor™ 25MB400 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 25MB400 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: Heat seal coextruded biaxially oriented polypropylene film that can be used on a wide range of packaging machines. 25MB400 can be either used as mono material or in laminated structures.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Outstanding optical propertiesGood seal strengthGood dimensional stabilityGood hot slipGood hot tackFeatures:In Lamination Lap SealableApplications:BakeryBiscuits/Cookie/CrackersBox OverwrapConfectionery, Chocolate Confectionery, Gum Confectionery, SugarCrisps and SnacksFresh ProduceFrozen FoodHealth and Beauty CareHousehold and DetergentsIce CreamPet Food Uses: HFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Outer Web Extrusion Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.10 g/m²/day @Temperature 23.0 °C	0.0710 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.97 g/m²/day @Temperature 38.0 °C	0.320 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Thickness	24.9 microns	0.980 mil	ExxonMobil Method
Coating Weight	22.4 g/m²	14.0 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	205 %	205 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	55 %	55 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.50 GPa	508 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.30	0.30	Both Sides; ExxonMobil Method
Seal Strength	300 g/25 mm @Pressure 0.0689 MPa, Temperature 115 °C	300 g/in @Pressure 10.0 psi, Temperature 239 °F	0.8 sec; ExxonMobl Method
	300 g/25 mm @Pressure 0.0689 MPa, Temperature 120 °C	300 g/in @Pressure 10.0 psi, Temperature 248 °F	ESM, 0.8 sec, Treated Surface; ExxonMobl Method
	300 g/25 mm @Pressure 0.0689 MPa, Temperature 115 °C	300 g/in @Pressure 10.0 psi, Temperature 239 °F	ESM, 0.8 sec, Untreated Surface; ExxonMobl Method
Film Tensile Strength at Break, MD	140 MPa	20300 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.0 % @Temperature 135 °C, Time 432 sec	5.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.8 %	1.8 %	ExxonMobil Method
Gloss	85 %	85 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	54°F	36.3 psi, 0.2 sec
Yield	30900 in²/lb