ExxonMobil Bicor™ 21MB866 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 21MB866 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 21MB866 is a high gas barrier, transparent biaxially oriented polypropylene film coated on side acrylic, one side PVOH. It provides excellent gas and aroma protection and is designed to be used as the outer web in modified atmosphere applications for dry products.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Excellent moisture, oxygen and aroma barriersExceptional gas and aroma barrierOutstanding optical propertiesLow sealing threshold and broad sealing range on acrylic sideIdeal support for normal ink systemsWater based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierGas BarrierIn Lamination Lap SealableOxygen BarrierPVOH Coated Applications:BakeryBiscuits/Cookie/Crackers Crisps and SnacksDairy ProductsDry Foods and Beverage Powders Pet Food Uses: HFFS Flexible Packaging VFFS Flexible Packaging Processing Method: Cold Seal Adhesive, Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing and Solvent Rotogravure PrintingInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 4.04 g/m²/day @Temperature 38.0 °C |
0.260 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method |
| Oxygen Transmission Rate | 0.698 cc/m²/day @Temperature 23.0 °C |
0.0450 cc/100 in²/day @Temperature 73.4 °F |
0% RH; ExxonMobil Method |
| Thickness | 21.1 microns | 0.830 mil | ExxonMobil Method |
| Coating Weight | 18.4 g/m² | 11.5 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 140 % | 140 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 50 % | 50 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Coefficient of Friction | 0.25 | 0.25 | Acrylic; ExxonMobil Method |
| Seal Strength | 510 g/25 mm @Pressure 0.276 MPa, Temperature 130 °C |
510 g/in @Pressure 40.0 psi, Temperature 266 °F |
Otto Bruger, 0.2 sec; ExxonMobl Method |
| Film Tensile Strength at Break, MD | 130 MPa | 18900 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 250 MPa | 36300 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % @Temperature 135 °C, Time 432 sec |
5.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 3.0 % @Temperature 135 °C, Time 432 sec |
3.0 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 0.90 % | 0.90 % | ExxonMobil Method |
| Gloss | 90 % | 90 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 72°F | 36.3 psi, 0.2 sec |
| Yield | 37600 in2/lb |