ExxonMobil Bicor® 140 BSR-ONE OPP Film
| Category | Polymer , Film , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor® 140 BSR-ONE OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor BSR-ONE is a two-side sealable, one side treated, coextruded OPP film designed for unsupported plain or surface print applications, and in laminations on both HFFS and VFFS packaging machines.Availability: Latin America, North America and South AmericaKey Features:Excellent machinablityStable COFExcellent hot tackExcellent hot slipExcellent hot jaw releaseExcellent heat seal strengthWide heat seal range on the untreated side (80°F/45°C)Non-migratory slip system for consistent COFFeatures:In Lamination Lap SealableApplications:BakeryBiscuts/Cookie/CrackersBox OverwrapConfectionery, GumConfectionery, SugarCrips and SnacksFrozen FoodPet FoodUses:Box Overwrap Flexible PackagingHFFS Flexible PackagingPre-made Bags – Flexible PackagingVFFS Flexible PackagingProcessing Method: Inner Web Adhesive Lamination, Outer Web Adhesive Lamination, Solvent Flexographic Printing, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 3.70 g/m²/day | 0.238 g/100 in²/day | 38°C, 90% RH; 518 |
| Thickness | 35.6 microns | 1.40 mil | Nominal |
| Coating Weight | 31.4 g/m² | 19.6 lb/ream | 520 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Coefficient of Friction | 0.34 | 0.34 | Treated; 430 |
| 0.39 | 0.39 | Untreated; 430 | |
| Film Tensile Strength at Break, MD | 114 MPa | 16500 psi | 20 in/min, 2.0 in Jaw Separation; 510 |
| Film Tensile Strength at Break, TD | 255 MPa | 37000 psi | 20 in/min, 2.0 in Jaw Separation; 510 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 5.0 % | 5.0 % | at 275°F; 438 |
| Shrinkage, TD | 4.5 % | 4.5 % | at 275°F; 438 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 2.3 % | 2.3 % | 444 |
| Gloss | 85 % | 85 % | 45°, Treated Surface; 442 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Crimp Seal MST | 216°F | untreated |
| 234°F | treated | |
| Crimp Seal Strength | 650, g/in | 250°F, 20psi, 3/4sec |
| Wetting Tension | 0.8receding COS theta | Treated Surface |
| Yield | 22000 in2/lb |
Users viewing this material also viewed the following:
- Greene Tweed CHEMRAZ® 653 Perfluoroelastomer
- Hexcel® HexForce™ 286 Carbon Fabric
- Covestro Baygal® 90 IK 51 Polyurethane
- Diamond Polymers PC 1001 GF30 30% Glass Reinforced Polycarbonate
- Adell BR-14 Nylon 6, 20% Glass Reinforced
- Aaron Industries AAROPRENE® AEPC 5000-3 Engineered Polycarbonate Resin
- ConocoPhillips Hydroclear® 50 Fluid
- BASF Neopolen® P 9230 K 0.06 g/cc Core density; Expanded Polypropylene (Europe)
- Haynes 25 alloy, room temperature after 20% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved