ExxonMobil AP03B Polypropylene Impact Copolymer

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil AP03B Polypropylene Impact Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: A high crystallinity, medium impact copolymer resin with high melt flow rate and excellent processing attributes. It is designed for injection molded large appliance applications and automotive interior parts.Availability: Asia Pacific Features:Fast Molding CycleGood ProcessabilityHigh FlowHigh StiffnessHighly CrystallineMedium Impact Resistance Uses: Appliance ComponentsAutomotive ApplicationsAutomotive Interior PartsConsumer ApplicationsIndustrial Applications Processing Method: Injection MoldingInformation provided by ExxonMobil
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ExxonMobil Method
Melt Flow 30 g/10 min

@Load 2.16 kg,
Temperature 230 °C
30 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 25.1 MPa
3640 psi
ISO 527-2/50
26.6 MPa
3860 psi
2.0 in/min; ASTM D638
Elongation at Yield 4.9 %
4.9 %
ISO 527-2/50
5.0 %
5.0 %
2.0 in/min; ASTM D638
Tensile Modulus 1.44 GPa
209 ksi
ISO527-2/1
Flexural Modulus 1.26 GPa
183 ksi
0.079 in/min; ISO 178
Flexural Modulus, 1% Secant 1310 MPa
190000 psi
0.05 in/min; ASTM D790A
1500 MPa
217000 psi
0.5 in/min; ASTM D790B
Izod Impact, Notched 0.342 J/cm

@Temperature -17.8 °C
0.640 ft-lb/in

@Temperature 0.000 °F
ASTM D256A
0.694 J/cm

@Temperature 22.8 °C
1.30 ft-lb/in

@Temperature 73.0 °F
ASTM D256A
Izod Impact, Notched (ISO) 2.94 kJ/m²

@Temperature -40.0 °C
1.40 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
3.99 kJ/m²

@Temperature -17.8 °C
1.90 ft-lb/in²

@Temperature 0.000 °F
ISO 180/1A
7.98 kJ/m²

@Temperature 22.8 °C
3.80 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 0.336 J/cm²

@Temperature -30.0 °C
1.60 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
0.378 J/cm²

@Temperature -20.0 °C
1.80 ft-lb/in²

@Temperature -4.00 °F
ISO 179/1eA
0.420 J/cm²

@Temperature 0.000 °C
2.00 ft-lb/in²

@Temperature 32.0 °F
ISO 179/1eA
0.756 J/cm²

@Temperature 22.8 °C
3.60 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 17.3 J

@Thickness 3.17 mm,
Temperature -28.9 °C
12.7 ft-lb

@Thickness 0.125 in,
Temperature -20.0 °F
Geometry GC; ASTM D5420
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 93.3 °C
200 °F
ISO 75-2/Bf
105 °C
221 °F
Unannealed; ASTM D648
119 °C
246 °F
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 54.4 °C
130 °F
ISO 75-2/A