Evonik Corporation Vestodur® CL2130 30% Glass Reinforced, Crosslinkable PBT Based Compound

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer Evonik Corporation
Trade Name Vestodur®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Evonik Corporation Vestodur® CL2130 30% Glass Reinforced, Crosslinkable PBT Based Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: VESTODUR CL2130 is a 30 % glass fiber reinforced, self-extinguishing compound for injection molding, based on modified polybutylene terephthalate (PBT).Moldings of VESTODUR CL2130 can be crosslinked by high-energy radiation (ß- or ?-radiation) or heat. The influence of the radiation to the mechanical properties is negligible. The short-term heat resistance is increased up to 350°C depending on the conditions. Crosslinked parts of VESTODUR CL2130 can be used in common soldering processes like surge soldering, vapor phase soldering, and IR soldering which are typical in the electronic industry. The incorporated flame retardant is non-migrating and has no corrosive effects on metal inserts or neighboring metal parts. Due to a special additive this PBT compound can be metallized selectively.Information provided by degussa.
Physical Properties Metric English Comments
Density 1.97 g/cc
0.0712 lb/in³
ISO 1183
Water Absorption at Saturation 0.40 %
0.40 %
ISO 62
Linear Mold Shrinkage 0.0010 cm/cm

@Thickness 2.00 mm
0.0010 in/in

@Thickness 0.0787 in
sheet with film gate at rim, mold temperature 80°C
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
Melt Flow 39.4 g/10 min

@Load 2.16 kg,
Temperature 250 °C
39.4 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527-1/2
Elongation at Break 1.1 %
1.1 %
ISO 527-1/2
Tensile Modulus 11.4 GPa
1650 ksi
ISO 527-1/-2
Charpy Impact Unnotched 3.50 J/cm²

@Temperature 23.0 °C
16.7 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75-1/-2
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
IEC 60695
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695
Electrical Properties Metric English Comments
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
IEC 60093
Dielectric Constant 5.0

@Frequency 1e+6 Hz
5.0

@Frequency 1e+6 Hz
IEC 60250
5.1

@Frequency 100 Hz
5.1

@Frequency 100 Hz
IEC 60250
Dissipation Factor 0.0090

@Frequency 100 Hz
0.0090

@Frequency 100 Hz
IEC 60250
0.020

@Frequency 1e+6 Hz
0.020

@Frequency 1e+6 Hz
IEC 60250
Comparative Tracking Index 150 V
150 V
100 drops value; IEC 60112
175 V
175 V
Test Solution A CTI; IEC 60112