Evonik Corporation Vestamid® L2141 Black Nylon 12

Category Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer Evonik Corporation
Trade Name Vestamid®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Evonik Corporation Vestamid® L2141 Black Nylon 12.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: High-viscosity, higher heat stability than L2140, light-stabilized, with processing aidApplications: Tubing for hydraulic clutches, vacuum linesInformation provided by degussa.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.70 %

@Thickness 1.00 mm,
Temperature 23.0 °C
0.70 %

@Thickness 0.0394 in,
Temperature 73.4 °F
50% R.H.; ISO 62
Water Absorption at Saturation 1.5 %

@Thickness 1.00 mm
1.5 %

@Thickness 0.0394 in
ISO 62
Linear Mold Shrinkage 0.012 cm/cm
0.012 in/in
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2)
Linear Mold Shrinkage, Transverse 0.014 cm/cm
0.014 in/in
127x12.7x3.2 mm (processing cond. acc. To ISO 1874-2)
Mechanical Properties Metric English Comments
Tensile Strength, Yield 46.0 MPa
6670 psi
ISO 527-1/2
Elongation at Break >= 50 %
>= 50 %
ISO 527-1/2
Elongation at Yield 5.0 %
5.0 %
ISO 527-1/2
Tensile Modulus 1.50 GPa
218 ksi
ISO 527-1/2
Charpy Impact Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²

@Temperature -30.0 °C
3.81 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.00 J/cm²

@Temperature 23.0 °C
4.76 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear 150 µm/m-°C

@Temperature 23.0 - 55.0 °C
83.3 µin/in-°F

@Temperature 73.4 - 131 °F
45x15x10 mm; ISO 11359
Melting Point 178 °C
352 °F
Peak Temperature; ISO 3146, ISO 11357
Deflection Temperature at 0.46 MPa (66 psi) 110 °C
230 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75
Vicat Softening Point 140 °C
284 °F
50N; ISO 306
170 °C
338 °F
10N; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
IEC 60093
Dielectric Constant 4.0

@Frequency 1e+6 Hz
4.0

@Frequency 1e+6 Hz
IEC 60250
9.7

@Frequency 100 Hz
9.7

@Frequency 100 Hz
IEC 60250
Dielectric Strength 35.0 kV/mm
889 kV/in
K20/P50; IEC 60243-1
Dissipation Factor 0.11

@Frequency 1e+6 Hz
0.11

@Frequency 1e+6 Hz
IEC 60250
0.21

@Frequency 100 Hz
0.21

@Frequency 100 Hz
IEC 60250
Comparative Tracking Index >= 600 V
>= 600 V
Test Solution A, 50 drops; IEC 60112
600 V
600 V
Test Solution A, 100 drops; IEC 60112
Descriptive Properties Value Comments
Electrolytic Corrosion A1 Step
IEC 60426