Evonik CYRO Acrylite® FT8 NTA Compound

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer Evonik CYRO
Trade Name Acrylite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Evonik CYRO Acrylite® FT8 NTA Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ISO 1183
Water Absorption <= 0.30 %
<= 0.30 %
ASTM D570
Linear Mold Shrinkage 0.0060 - 0.0070 cm/cm
0.0060 - 0.0070 in/in
ISO 294
Melt Flow 3.5 g/10 min

@Load 3.80 kg,
Temperature 230 °C
3.5 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell M 95
95
ASTM D785
Tensile Strength at Break 74.001 MPa
10733 psi
ISO 527
Elongation at Break 4.0 %
4.0 %
ISO 527
Elongation at Yield 4.0 %
4.0 %
ISO 527
Tensile Modulus 3.24 GPa
470 ksi
ISO 527
Flexural Strength 95.403 MPa
13837 psi
ISO 178
Flexural Modulus 3.10 GPa
450 ksi
ISO 178
Izod Impact, Unnotched (ISO) 2.00 kJ/m²

@Diameter 4.00 mm
0.952 ft-lb/in²

@Diameter 0.157 in
bar; ISO 180
Thermal Properties Metric English Comments
CTE, linear 75.6 µm/m-°C

@Temperature 0.000 - 100 °C
42.0 µin/in-°F

@Temperature 32.0 - 212 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 101 °C
214 °F
annealed; ISO 75
Vicat Softening Point 106 °C
223 °F
ISO 306
Optical Properties Metric English Comments
Transmission, Visible 0.0 %
0.0 %
Opaque; ASTM D1003
Processing Properties Metric English Comments
Middle Barrel Temperature 210 - 249 °C
410 - 480 °F
Cylinder Temp
Melt Temperature 238 - 249 °C
460 - 480 °F
Mold Temperature 37.8 - 79.4 °C
100 - 175 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 2 - 3 hour
2 - 3 hour