Evonik CYRO Acrylite® FT15 NTA Compound

Category Polymer , Thermoplastic , Acrylic (PMMA) , Acrylic, Impact Modified, Molded
Manufacturer Evonik CYRO
Trade Name Acrylite®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Evonik CYRO Acrylite® FT15 NTA Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ISO 1183
Water Absorption <= 0.30 %
<= 0.30 %
ASTM D570
Linear Mold Shrinkage 0.0050 - 0.0060 cm/cm
0.0050 - 0.0060 in/in
ISO 294
Melt Flow 2.2 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.2 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 57.9 MPa
8400 psi
ISO 527
Elongation at Break 1.9 %
1.9 %
ISO 527
Elongation at Yield 1.9 %
1.9 %
ISO 527
Tensile Modulus 3.52 GPa
510 ksi
ISO 527
Flexural Strength 62.7 MPa
9100 psi
ISO 178
Flexural Modulus 3.38 GPa
490 ksi
ISO 178
Izod Impact, Unnotched (ISO) 1.90 kJ/m²

@Diameter 4.00 mm
0.904 ft-lb/in²

@Diameter 0.157 in
bar; ISO 180
Thermal Properties Metric English Comments
CTE, linear 72.0 µm/m-°C

@Temperature 0.000 - 100 °C
40.0 µin/in-°F

@Temperature 32.0 - 212 °F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
annealed; ISO 75
Vicat Softening Point 113 °C
235 °F
ISO 306
Optical Properties Metric English Comments
Transmission, Visible 0.0 %
0.0 %
Opaque; ASTM D1003
Processing Properties Metric English Comments
Middle Barrel Temperature 221 - 249 °C
430 - 480 °F
Cylinder Temp
Melt Temperature 221 - 249 °C
430 - 480 °F
Mold Temperature 48.9 - 96.1 °C
120 - 205 °F
Drying Temperature 105 °C
221 °F
Dry Time 2 - 3 hour
2 - 3 hour