Eurotec® Tecomid® NB30 BK EF PA6, unfilled, black, suitable for electrostatic powder coating

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer Eurotec
Trade Name Tecomid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurotec® Tecomid® NB30 BK EF PA6, unfilled, black, suitable for electrostatic powder coating.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Eurotec®
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 2.50 %

@Temperature 23.0 °C
2.50 %

@Temperature 73.4 °F
50% RH; ISO 960
Linear Mold Shrinkage, Flow 0.011 cm/cm
0.011 in/in
Eurotec
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
Eurotec
Mechanical Properties Metric English Comments
Tensile Strength at Break 70.0 MPa
10200 psi
ISO 527
Tensile Modulus 3.00 GPa
435 ksi
ISO 527
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
7.00 kJ/m²

@Temperature 23.0 °C
3.33 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
Melting Point 223 °C
433 °F
[10 K/min], ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+05
<= 1e+05
IEC 60093
Processing Properties Metric English Comments
Processing Temperature 240 - 260 °C
464 - 500 °F
Feed Temperature 60.0 - 80.0 °C
140 - 176 °F
Throat
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.20 %
<= 0.20 %
ISO 960
Hold Pressure 50.0 - 100 MPa
7250 - 14500 psi
Descriptive Properties Value Comments
Back Pressure Low
Injection Speed Medium - Fast