- Eurotec® Tecolen® HP10 GR20 NL PPCP, 20% glass fiber reinforced, natural
Eurotec® Tecolen® HP10 GR20 NL PPCP, 20% glass fiber reinforced, natural
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 20% Glass Fiber Filler |
| Manufacturer | Eurotec |
| Trade Name | Tecolen® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecolen® HP10 GR20 NL PPCP, 20% glass fiber reinforced, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 5.00 GPa | 725 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 170 °C | 329 - 338 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 240 °C | 392 - 464 °F | |
| Feed Temperature | <= 60.0 °C | <= 140 °F | Throat |
| Mold Temperature | 20.0 - 50.0 °C | 68.0 - 122 °F | |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- Multibase TPSiV™ 1180-50D Thermoplastic Silicone Vulcanizate
- SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS
- Polykemi AB POLYelast TPE ZS706 Thermoplastic Elastomer, SEBS/SBS-based
- Solvay TECHNYL® B 218 Black 21 N PA66/6, Conditioned
- Samyang Trirex® 3030IR Polycarbonate
- Solvay TOLCIDE® PS 75LT 75% tetrakis hydroxymethyl phosphonium sulfate
- Borealis Borstar® FB4250T LLDPE for Blown Film
- DuPont™ Appeel® 72D811 Sealing Resin
- Arlon 48576R006 0.0055" Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved