Eurotec® Tecoform® PO20 GR10 NL HS POM, 10% glass fiber reinforced, heat stabilized, natural

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 10% Glass Fiber Reinforced
Manufacturer Eurotec
Trade Name Tecoform®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurotec® Tecoform® PO20 GR10 NL HS POM, 10% glass fiber reinforced, heat stabilized, natural.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Eurotec®
Physical Properties Metric English Comments
Density 1.47 g/cc
0.0531 lb/in³
ISO 1183
Moisture Absorption 0.200 %

@Temperature 23.0 °C
0.200 %

@Temperature 73.4 °F
50% RH; ISO 960
Linear Mold Shrinkage, Flow 0.0050 cm/cm
0.0050 in/in
Eurotec
Linear Mold Shrinkage, Transverse 0.018 cm/cm
0.018 in/in
Eurotec
Mechanical Properties Metric English Comments
Tensile Strength at Break 90.0 MPa
13100 psi
ISO 527
Elongation at Break 4.0 %
4.0 %
ISO 527
Tensile Modulus 4.50 GPa
653 ksi
ISO 527
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature -30.0 °C
2.38 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
6.00 kJ/m²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Thermal Properties Metric English Comments
Melting Point 165 °C
329 °F
[10 K/min], ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
ISO 75
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+14 ohm-cm
1.00e+14 ohm-cm
IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
IEC 60093
Comparative Tracking Index 500 V
500 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Processing Temperature 190 - 230 °C
374 - 446 °F
Feed Temperature 30.0 - 50.0 °C
86.0 - 122 °F
Throat
Mold Temperature 60.0 - 120 °C
140 - 248 °F
Drying Temperature 100 - 120 °C
212 - 248 °F
Dry Time 3.00 - 6.00 hour
3.00 - 6.00 hour
Hold Pressure 80.0 - 100 MPa
11600 - 14500 psi
Descriptive Properties Value Comments
Back Pressure Low
Injection Speed Medium - Fast