Eurostar Starpylen HT 25 MC PP, Mineral Filled, Injection Molding
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starpylen |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starpylen HT 25 MC PP, Mineral Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starpylen HT 25 MC is a Mineral Filled Polypropylene Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 - 0.016 cm/cm @Thickness 4.00 mm |
0.012 - 0.016 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ISO 527 |
| Elongation at Break | 40 % | 40 % | |
| Tensile Modulus | 2.40 GPa | 348 ksi | ISO 527 |
| Flexural Strength | 55.0 MPa | 7980 psi | ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80x10x4; ISO 180/1A |
| Charpy Impact Unnotched | 2.50 J/cm² | 11.9 ft-lb/in² | Edgew 80x10x4 sp=62; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Vicat Softening Point | 149 °C | 300 °F | B/50; ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 220 °C | 428 °F | |
| Zone 2 | 230 °C | 446 °F | |
| Zone 3 | 240 °C | 464 °F | |
| Melt Temperature | 210 - 250 °C | 410 - 482 °F | |
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Quantum Composites QC-7810 55% Glass Fiber Polyester SMC (discontinued **)
- SABIC Innovative Plastics XYLEX X7509HP PC+POLYESTER (Europe-Africa-Middle East)
- Techmer ES Luriblend® PE 5903
- Master Bond EP30FL Low Viscosity, Flexibilized Two Component Epoxy
- Dow Corning SYL-OFF® PMCPSL 9111 Coating
- Ceradyne Ceralloy® 147-1B Reaction Bonded Silicon Nitride (Si3N4)
- Solvay Specialty Polymers Diofan® A 036 Polyvinylidene Chloride (PVDC) (discontinued **)
- Formosa Plastics Formolene® 5140L Homopolymer Polypropylene
- Solvay RHODASURF® 870 Surfactant
Copyright © lookpolymers.com All Rights Reserved