- Eurostar Starglas CF006 Styrenic, 30% Glass Filled, Injection Molding
Eurostar Starglas CF006 Styrenic, 30% Glass Filled, Injection Molding
| Category | Polymer , Thermoplastic , Polystyrene (PS) |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starglas |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starglas CF006 Styrenic, 30% Glass Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starglas CF006 is a 30% Glass Fiber Reinforced Styrenic Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 69.0 MPa | 10000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 180 - 230 °C | 356 - 446 °F | |
| Zone 2 | 200 - 240 °C | 392 - 464 °F | |
| Zone 3 | 200 - 240 °C | 392 - 464 °F | |
| Melt Temperature | 200 - 240 °C | 392 - 464 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Drying Temperature | 70.0 °C @Time 10800 sec |
158 °F @Time 3.00 hour |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 3-8277 Polyamide 6, unreinforced
- Hyosung Topilene HJ145 PP
- LyondellBasell Lupolen® 1812 D LDPE
- Taiwan PU Corporation PTMG CPU-167L Polyurethane Casting Elastomer
- Solvay Specialty Polymers Ryton® R-4XT Polyphenylene Sulfide (PPS), 40% Glass Fiber
- Teknor Apex Monprene® MP 1225B Thermoplastic Elastomer
- A. Schulman POLYTROPE™ TPP 608 Olefinic Elastomer
- ExxonMobil Greasrex K-218
- ChevronTexaco Bright-Cut® NL Metal Working Fluid
- Asahi Kasei Thermofil P-40CC-1100 40% Calcium Carbonate Reinforced, Heat Stabilized
Copyright © lookpolymers.com All Rights Reserved