Eurostar Starflam RF0057P PA66/6, 25% Glass Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam RF0057P PA66/6, 25% Glass Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Starflam RF0057P is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66/6 Injection Molding Resin (also known as RF1005Z270EM)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.39 g/cc
0.0502 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 130 MPa
18900 psi
5 mm/min; ISO 527
Elongation at Break 2.4 %
2.4 %
5 mm/min; ISO 527
Flexural Strength 195 MPa
28300 psi
2 mm/min; ISO 178
Flexural Modulus 8.10 GPa
1170 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Hot Ball Pressure Test 200 °C

@Thickness 3.00 mm
392 °F

@Thickness 0.118 in
IEC 60695-10-2
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 140 °C

@Thickness 0.800 mm
284 °F

@Thickness 0.0315 in
140 °C

@Thickness 1.60 mm
284 °F

@Thickness 0.0630 in
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 105 °C

@Thickness 0.800 mm
221 °F

@Thickness 0.0315 in
105 °C

@Thickness 1.60 mm
221 °F

@Thickness 0.0630 in
105 °C

@Thickness 3.00 mm
221 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 140 °C

@Thickness 0.800 mm
284 °F

@Thickness 0.0315 in
140 °C

@Thickness 1.60 mm
284 °F

@Thickness 0.0630 in
140 °C

@Thickness 3.00 mm
284 °F

@Thickness 0.118 in
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
IEC 60695-11-10
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
IEC 60695-11-10
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
IEC 60695-11-10
Glow Wire Test 775 °C

@Thickness 0.800 mm
1430 °F

@Thickness 0.0315 in
Glow-Wire Ignition; IEC 60695-2-13
800 °C

@Thickness 1.60 mm
1470 °F

@Thickness 0.0630 in
Glow-Wire Ignition; IEC 60695-2-13
825 °C

@Thickness 3.00 mm
1520 °F

@Thickness 0.118 in
Glow-Wire Ignition; IEC 60695-2-13
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
Glow-Wire Flammability; IEC 60695-2-12
960 °C

@Thickness 1.60 mm
1760 °F

@Thickness 0.0630 in
Glow-Wire Flammability; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow-Wire Flammability; IEC 60695-2-12
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V

@Thickness 3.00 mm
600 V

@Thickness 0.118 in
IEC 60112
Hot Wire Ignition, HWI >= 120 sec

@Thickness 0.800 mm
>= 120 sec

@Thickness 0.0315 in
PLC 0
>= 120 sec

@Thickness 1.60 mm
>= 120 sec

@Thickness 0.0630 in
PLC 0
>= 120 sec

@Thickness 3.00 mm
>= 120 sec

@Thickness 0.118 in
PLC 0
High Amp Arc Ignition, HAI >= 120 arcs

@Thickness 0.800 mm
>= 120 arcs

@Thickness 0.0315 in
PLC 0
>= 120 arcs

@Thickness 1.60 mm
>= 120 arcs

@Thickness 0.0630 in
PLC 0
>= 120 arcs

@Thickness 3.00 mm
>= 120 arcs

@Thickness 0.118 in
PLC 0
Processing Properties Metric English Comments
Rear Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 1
Middle Barrel Temperature 265 - 275 °C
509 - 527 °F
Zone 2
Front Barrel Temperature 270 - 280 °C
518 - 536 °F
Zone 3
Melt Temperature 270 - 280 °C
518 - 536 °F
Mold Temperature 60.0 - 100 °C
140 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %