Eurostar Starflam PK0022E PA6, 10% Mineral Filled, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled
Manufacturer Eurostar Engineering Plastics
Trade Name Starflam
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Starflam PK0022E PA6, 10% Mineral Filled, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PK0022E is a Halogen Free and Phosphorous Free, Mineral Filed, Polyamide 6 Injection Molding (also known as PM3620Z22 or PA 10E6 U9 Z22)Information provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.012 - 0.014 cm/cm
0.012 - 0.014 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 69.0 MPa
10000 psi
5 mm/min; ISO 527
Elongation at Break 3.1 %
3.1 %
5 mm/min; ISO 527
Flexural Strength 102 MPa
14800 psi
2 mm/min; ISO 178
Flexural Modulus 3.40 GPa
493 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80x10x4; ISO 180/1A
Izod Impact, Unnotched (ISO) 25.0 kJ/m²
11.9 ft-lb/in²
80x10x4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 71.0 °C
160 °F
Flatw 80x10x4, sp=64 mm; ISO 75/Af
UL RTI, Electrical 65.0 °C

@Thickness 1.60 mm
149 °F

@Thickness 0.0630 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 1.60 mm
149 °F

@Thickness 0.0630 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 1.60 mm
149 °F

@Thickness 0.0630 in
Flammability, UL94 V-2

@Thickness 1.60 mm
V-2

@Thickness 0.0630 in
IEC 60695-11-10
Processing Properties Metric English Comments
Rear Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 1
Middle Barrel Temperature 250 - 260 °C
482 - 500 °F
Zone 2
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Zone 3
Melt Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 50.0 - 90.0 °C
122 - 194 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content 0.20 %
0.20 %