- Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded
Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide RFB53U PA66, 50% Glass Bead/Fiber Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
RFB53U is a Glass Bead/ Glass Fiber Reinforced Polyamide 66 Injection Molding Resin (also known as Staramide 66 1525 VK Z4)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | 1.1 % @Temperature 23.0 °C, Time 86400 sec |
1.1 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 4.00 mm |
0.0070 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 131 MPa | 19000 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 201 MPa | 29200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80x10x4; ISO 179/1eA |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² | 14.3 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 42.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
23.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 86.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
47.8 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 290 °C | 518 - 554 °F | |
| Zone 3 | 280 - 290 °C | 536 - 554 °F | |
| Melt Temperature | 275 - 285 °C | 527 - 545 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- NOVA Chemicals Novapol® LF-0225-B LDPE Clarity Film Resin (discontinued **)
- Chevron Phillips HiD® 9506 HDPE Blow Molding Resin (discontinued **)
- Momentive Performance Materials RTV577 White Extreme Low Temperature Potting/Encapsulating Compound
- Ineos ABS Lustran® Ultra 4105 ABS Pellets (Polycarbonate-modified), Medium High Heat Grade
- Saint-Gobain Norton® ETFE Fluoropolymer Film
- A. Schulman POLYBATCH™ Brown 10305U Concentrate Based In LLDPE
- Master Bond UV25 One component, moderate viscosity UV curable system
- ExxonMobil Medium Mobil DTE Oil Named Series
- Dow VORANOL™ 4701 Polyether Polyol
- Bhansali Engineering Abstron IM-17 A EP ABS Electro Plating Applications
Copyright © lookpolymers.com All Rights Reserved