Eurostar Staramide PFB42U PA6, Glass Fiber/Bead Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 10% Glass Fiber Filled , Nylon 6, Glass Bead Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide PFB42U PA6, Glass Fiber/Bead Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam PFB42U is an UV Stabilized, Glass Bead and Glass Fiber Reinforced Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm @Thickness 4.00 mm |
0.0050 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ISO 527 |
| Flexural Strength | 140 MPa | 20300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 4.40 GPa | 638 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | Annealed 120°C/2hr; ISO 75/Ae |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 230 - 240 °C | 446 - 464 °F | |
| Zone 2 | 240 - 260 °C | 464 - 500 °F | |
| Zone 3 | 240 - 270 °C | 464 - 518 °F | |
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Ensinger ENSITEP® PBT Polybutylene Terephthalate - Extruded Products (discontinued **)
- Solvay Engineered Polymers SEQUEL® 1733HI Engineered Polyolefin (discontinued **)
- Karina 552-48/1-DT-IE Compound PVC Black
- Haynes Hastelloy® C-22® alloy, transverse, GTAW weldment, sheet - plate
- Teknor Apex Telcar® TL-2635A Thermoplastic Elastomer
- Chengdu Polyster KP-200-30 Silicone Masterbatch
- Clariant Renol 6601FR Nylon 66, Flame Retardant
- Dow Corning 2-3899 Antifoam Compound
- ACC MMAD25 Addition Cure 2-Part Molding Rubber
Copyright © lookpolymers.com All Rights Reserved