Eurostar Staramide P1000IX1 PA6, Impact Modified, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Staramide |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Staramide P1000IX1 PA6, Impact Modified, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Staramide P1000IX1 is an Impact Modified, Polyamide 6 Injection Molding Resin (also known as P1000HI006 or Star X 2006)Information provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.023 cm/cm @Thickness 4.00 mm |
0.023 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 44.0 MPa | 6380 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527 |
| Elongation at Yield | 3.8 % | 3.8 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.50 GPa | 363 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 65.0 MPa | 9430 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.70 GPa | 247 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB | NB | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 145 °C | 293 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 220 - 230 °C | 428 - 446 °F | |
| Zone 2 | 230 - 240 °C | 446 - 464 °F | |
| Zone 3 | 240 - 250 °C | 464 - 482 °F | |
| Melt Temperature | 240 - 250 °C | 464 - 482 °F | |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | |
| Drying Temperature | 75.0 - 85.0 °C @Time 14400 - 21600 sec |
167 - 185 °F @Time 4.00 - 6.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Polimeri Europa Riblene® MY 00 Low Density Polyethylene - Injection Molding
- Nilit FRIANYL B63 HS-KV30 Nylon 6 for injection molding, 30% glass ball reinforced
- Iran Petrochemical (PCC) 52511 High Density Polyethylene
- Haynes 230® alloy, 10% cold reduction
- SABIC Innovative Plastics Valox® V9500GW PET+PC (Europe-Africa-Middle East)
- Sibur SKS-30 ARKM-27 1st Group Oil-Filled Styrene-Butadiene Rubber
- Solvay TECHNYL® AR 218 V25 Nylon 66, 25% glass fiber, DRY
- ChevronTexaco 13 SG Diesel Engine Oil
- DuPont Performance Polymers Sorona® 3301V NC010 Polytrimethylene Terephthalate (PTT)
- Beijing Evergrow Resources PTFE, 15% Glass Fiber, 10% Polyimide, 5% Graphite Filled
Copyright © lookpolymers.com All Rights Reserved