Eurostar Staramide A40 PA66, Extrusion

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Extruded
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide A40 PA66, Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Staramide A40 is Unreinforced, High Viscosity Polyamide 66, Extrusion ResinInformation provided by Eurostar.
Physical Properties Metric English Comments
Density 1.16 g/cc
0.0419 lb/in³
ISO 1183
Water Absorption at Saturation 6.5 %

@Temperature 23.0 °C
6.5 %

@Temperature 73.4 °F
ISO 62-1
Linear Mold Shrinkage, Flow 0.016 - 0.020 cm/cm
0.016 - 0.020 in/in
on Tensile Bar; E2P method
Mechanical Properties Metric English Comments
Hardness, Rockwell R 117
117
ISO 2039-2
Elongation at Break >= 30 %
>= 30 %
50 mm/min; ISO 527
Elongation at Yield 80 %
80 %
50 mm/min; ISO 527
Tensile Modulus 2.80 GPa
406 ksi
1 mm/min; ISO 527
Flexural Yield Strength 110 MPa
16000 psi
2 mm/min; ISO 178
Flexural Modulus 3.00 GPa
435 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 3.00 kJ/m²

@Temperature -40.0 °C
1.43 ft-lb/in²

@Temperature -40.0 °F
80x10x4; ISO 180/1A
4.00 kJ/m²

@Temperature -20.0 °C
1.90 ft-lb/in²

@Temperature -4.00 °F
80x10x4; ISO 180/1A
5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80x10x4; ISO 180/1A
Charpy Impact Unnotched >= 10.0 J/cm²
>= 47.6 ft-lb/in²
Edgew 80x10x4 sp=62; ISO 179/1eU
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 140 °F
ISO 11359-2
Hot Ball Pressure Test 123 - 127 °C
253 - 261 °F
IEC 60695-10-2
Deflection Temperature at 0.46 MPa (66 psi) 230 °C
446 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C
194 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Ae
Vicat Softening Point 252 °C
486 °F
B/120; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Oxygen Index 26 %
26 %
ISO 4589
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
600 V
600 V
M; IEC 60112
Processing Properties Metric English Comments
Zone 1 260 - 270 °C
500 - 518 °F
Zone 2 270 - 280 °C
518 - 536 °F
Zone 3 270 - 290 °C
518 - 554 °F
Melt Temperature 270 - 290 °C
518 - 554 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C

@Time 14400 - 21600 sec
167 - 185 °F

@Time 4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %