Epoxy Technology EPO-TEK® OE101 Two Component Epoxy

Category Polymer , Thermoset , Epoxy
Manufacturer Epoxy Technology
Trade Name EPO-TEK®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Epoxy Technology EPO-TEK® OE101 Two Component Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Material Description: A two component epoxy designed for low stress applications in fiber optic packaging, opto-electronics and semiconductors. It is a lower modulus version of EPO-TEK® 353ND.Information Provided by Epoxy Technology
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
Part B
1.16 g/cc
1.16 g/cc
Part A
Viscosity 1500 - 2500 cP

@Temperature 23.0 °C
1500 - 2500 cP

@Temperature 73.4 °F
100 rpm
Mechanical Properties Metric English Comments
Hardness, Shore D 82
82
Tensile Modulus 2.47 GPa
359 ksi
Storage
Shear Strength >= 13.8 MPa
>= 2000 psi
Lap
>= 35.2 MPa
>= 5100 psi
Die
Thermal Properties Metric English Comments
CTE, linear 41.0 µm/m-°C
22.8 µin/in-°F
Below Tg
210 µm/m-°C
117 µin/in-°F
Above Tg
Maximum Service Temperature, Air 200 °C
392 °F
Continuous
300 °C
572 °F
Intermittent
Minimum Service Temperature, Air -55.0 °C
-67.0 °F
Continuous
-55.0 °C
-67.0 °F
Intermittent
Glass Transition Temp, Tg >= 65.0 °C
>= 149 °F
Dynamic Cure 20—200°C /ISO 25 Min; Ramp 10—200°C @ 20°C/Min
Decomposition Temperature 456 °C
853 °F
Degradation Temperature
Optical Properties Metric English Comments
Refractive Index 1.5459

@Wavelength 589 nm
1.5459

@Wavelength 589 nm
uncured
Transmission, Visible >= 50 %

@Wavelength 400 nm
>= 50 %

@Wavelength 400 nm
Spectral
>= 92 %

@Wavelength 600 nm
>= 92 %

@Wavelength 600 nm
Spectral
>= 97 %

@Wavelength 675 nm
>= 97 %

@Wavelength 675 nm
Spectral
Electrical Properties Metric English Comments
Volume Resistivity >= 1.50e+13 ohm-cm
>= 1.50e+13 ohm-cm
Dielectric Constant 3.22

@Frequency 1000 Hz
3.22

@Frequency 1000 Hz
Dissipation Factor 0.0036

@Frequency 1000 Hz
0.0036

@Frequency 1000 Hz
Processing Properties Metric English Comments
Cure Time 1.00 min

@Temperature 150 °C
0.0167 hour

@Temperature 302 °F
minimum
5.00 min

@Temperature 125 °C
0.0833 hour

@Temperature 257 °F
minimum
10.0 min

@Temperature 100 °C
0.167 hour

@Temperature 212 °F
minimum
30.0 min

@Temperature 80.0 °C
0.500 hour

@Temperature 176 °F
minimum
Pot Life 240 min
240 min
Shelf Life 12.0 Month

@Temperature 25.0 °C
12.0 Month

@Temperature 77.0 °F
Descriptive Properties Value Comments
Color Amber
Part B
Clear Yellow
Part A
Consistency Pourable liquid
Mix Ratio By Weight 10:1
Number of Components Two
Weight Loss 0.6%
200°C
0.82%
250°C
1.22%
300°C