Epoxy Technology EPO-TEK® M10-D Epoxy Paste

Category	Polymer , Thermoset , Epoxy
Manufacturer	Epoxy Technology
Trade Name	EPO-TEK®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Epoxy Technology EPO-TEK® M10-D Epoxy Paste.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Material Description: A single component, B-stageable epoxy paste for semiconductor, microelectronics, and optical assemblies. It can be used in hybrid assemblies for lid-sealing and substrate attach. In opto-packaging, it can be used as the main gasket seal of glass plates in LCDs, or for sealing filter windows onto opto-sensors.Information Provided by Epoxy Technology

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc
Particle Size	<= 20 µm	<= 20 µm
Viscosity	3000 - 6000 cP @Temperature 23.0 °C	3000 - 6000 cP @Temperature 73.4 °F	50 rpm

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	72	72
Tensile Modulus	3.98 GPa	577 ksi	Storage
Shear Strength	4.00 MPa	580 psi	Lap
	>= 23.4 MPa	>= 3400 psi	Die

Thermal Properties	Metric	English	Comments
CTE, linear	35.0 µm/m-°C	19.4 µin/in-°F	Below Tg
	128 µm/m-°C	71.1 µin/in-°F	Above Tg
Maximum Service Temperature, Air	200 °C	392 °F	Continuous
	300 °C	572 °F	Intermittent
Minimum Service Temperature, Air	-55.0 °C	-67.0 °F	Continuous
	-55.0 °C	-67.0 °F	Intermittent
Glass Transition Temp, Tg	80.0 °C	176 °F
Decomposition Temperature	370 °C	698 °F	Degradation Temperature

Electrical Properties	Metric	English
Volume Resistivity	>= 5.00e+11 ohm-cm	>= 5.00e+11 ohm-cm
Dielectric Constant	4.32 @Frequency 1000 Hz	4.32 @Frequency 1000 Hz
Dissipation Factor	0.114 @Frequency 1000 Hz	0.114 @Frequency 1000 Hz

Processing Properties	Metric	English	Comments
Cure Time	30.0 min @Temperature 75.0 °C	0.500 hour @Temperature 167 °F	minimum
Pot Life	20160 min	20160 min
Shelf Life	12.0 Month	12.0 Month	refrigerated

Descriptive Properties	Value	Comments
Color	Tan	before cure
Consistency	Smooth thixotropic paste
Number of Components	Single
Weight Loss	1.13%	200°C
	2.76%	250°C
	5.75%	300°C