Epoxy Technology EPO-TEK® 310M-T Flexible Epoxy

Category Polymer , Thermoset , Epoxy
Manufacturer Epoxy Technology
Trade Name EPO-TEK®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Epoxy Technology EPO-TEK® 310M-T Flexible Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Material Description: A two component, flexible epoxy designed for low stress applications in semiconductor, hybrid, medical, acoustical and optical industries. Replacement for EPO-TEK® 310T.Information Provided by Epoxy Technology
Physical Properties Metric English Comments
Specific Gravity 1.08 g/cc
1.08 g/cc
Part B
1.12 g/cc
1.12 g/cc
Part A
Particle Size <= 20 µm
<= 20 µm
Viscosity 1800 - 3300 cP

@Temperature 23.0 °C
1800 - 3300 cP

@Temperature 73.4 °F
100 rpm
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
Tensile Modulus 0.008432 GPa
1.223 ksi
Storage
Shear Strength 3.45 MPa
500 psi
Lap
>= 7.03 MPa
>= 1020 psi
Die
Thermal Properties Metric English Comments
CTE, linear 74.0 µm/m-°C
41.1 µin/in-°F
Below Tg
236 µm/m-°C
131 µin/in-°F
Above Tg
Maximum Service Temperature, Air 200 °C
392 °F
Continuous
300 °C
572 °F
Intermittent
Minimum Service Temperature, Air -55.0 °C
-67.0 °F
Continuous
-55.0 °C
-67.0 °F
Intermittent
Glass Transition Temp, Tg <= 30.0 °C
<= 86.0 °F
Dynamic Cure 20—200°C /ISO 25 Min; Ramp 10—200°C @ 20°C/Min
Decomposition Temperature 401 °C
754 °F
Degradation Temperature
Electrical Properties Metric English Comments
Volume Resistivity >= 2.50e+10 ohm-cm
>= 2.50e+10 ohm-cm
Dielectric Constant 5.1

@Frequency 1000 Hz
5.1

@Frequency 1000 Hz
Dissipation Factor 0.091

@Frequency 1000 Hz
0.091

@Frequency 1000 Hz
Processing Properties Metric English Comments
Cure Time 120 min

@Temperature 65.0 °C
2.00 hour

@Temperature 149 °F
1440 min

@Temperature 23.0 °C
24.0 hour

@Temperature 73.4 °F
Pot Life 35 min
35 min
Shelf Life 12.0 Month

@Temperature 25.0 °C
12.0 Month

@Temperature 77.0 °F
Descriptive Properties Value Comments
Color Clear/Colorless
Part B
Tan
Part A
Consistency Slightly thixotropic paste
Mix Ratio By Weight 10:6
Number of Components Two
Weight Loss 0.05%
200°C
0.18%
250°C
0.63%
300°C