Ensinger Tecapeek® Polyetheretherketone (PEEK)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Ensinger |
| Trade Name | Tecapeek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ensinger Tecapeek® Polyetheretherketone (PEEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tecapeek™, made from Victrex PEEK polymer, is an excellent material for a wide spectrum of applications where thermal, chemical, and combustion properties are critical to performance.Excellent flexural, impact, and tensile characteristics Very high continuous working temp Very high heat distortion tempExceptional chemical resistance Superior dielectric at high temperatures and frequencies Good radiation resistanceOutstanding wear and abrasion resistance Low smoke and toxic gas emissions Excellent hydrolysis resistance Information provided by Ensinger, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 99 | 99 | ASTM D785 |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Elongation at Yield | 4.9 % | 4.9 % | ASTM D638 |
| Tensile Modulus | 4.482 GPa | 650.0 ksi | 1 % Sec; ASTM D638 |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| Flexural Modulus | 4.14 GPa | 600 ksi | Tangent; ASTM D790 |
| Compressive Strength | 118 MPa | 17100 psi | ASTM D695 |
| Shear Strength | 52.4 MPa | 7600 psi | Ultimate; ASTM D3846 |
| Izod Impact, Notched | 0.828 J/cm | 1.55 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.18 | 0.18 | 1200 in/min, 155 lbs Load; ASTM D1894-95 |
| Limiting Pressure Velocity | 5.96 MPa-m/sec | 170000 psi-ft/min | 1200 in/min |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 46.8 µm/m-°C @Temperature 20.0 °C |
26.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | 0.245 W/m-K | 1.70 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 334 °C | 633 °F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | Continuous |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.90e+16 ohm-cm | 4.90e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 19.7 kV/mm | 500 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP LUBRILOY RF203XXH PA 66
- Shandong Dongyue Polymer DF-302 PTFE Aqueous Dispersion 60%
- Unitika elitel UE3210 Polyester, Pellet
- Borealis BorPURE™ RD208CF Polypropylene Random Copolymer
- ThyssenKrupp FR-30® Fire Resistant Steel
- Epoxyset Epoxiohm EO-23M Electrically Conductive Epoxy Adhesive
- Ensinger TECAFLON™ PVDF Polyvinylidene Fluoride (PVDF) - extruded products
- BASF Ultramid® SEG7 35% Glass Filled PA6 (Dry)
- Hexion Bakelite™ PF 4260 Phenolic Formaldehyde Resin, Resistant to High Temperatures, Improved Electrical Properties, Low Shrinkage, High Mechanical Strength
Copyright © lookpolymers.com All Rights Reserved