- Ensinger Tecanat™ GF20 20% Glass Reinforced Polycarbonate (PC)
Ensinger Tecanat™ GF20 20% Glass Reinforced Polycarbonate (PC)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Ensinger |
| Trade Name | Tecanat™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ensinger Tecanat™ GF20 20% Glass Reinforced Polycarbonate (PC).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tenacat™ GF20 is typically used in business equipment where gears, rollers, interlam mechanical parts, connectors and relays are required. The automotive industry uses polycarbonate materials for pumps, valves, light bezels and instrument panels. Excellent dimensional stability Transparency Good machinabilityInformation provided by Ensinger, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | |
| Water Absorption | 0.16 % | 0.16 % | at 24 hours; ASTM D570 |
| Water Absorption at Saturation | 0.29 % | 0.29 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 110 MPa | 16000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 5.93 GPa | 860 ksi | ASTM D638 |
| Flexural Strength | 131 MPa | 19000 psi | ASTM D790 |
| Flexural Modulus | 5.50 GPa | 798 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Coefficient of Friction, Dynamic | 0.22 | 0.22 | 40 psi, 50 fpm; ASTM D3702 |
| K (wear) Factor | 242 x 10-8 mm³/N-M | 120 x 10-10 in³-min/ft-lb-hr | 40 psi, 50 fpm; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 27.0 µm/m-°C @Temperature 20.0 °C |
15.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Long Term; ASTM UL746B |
| 132 °C | 270 °F | Intermittent | |
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Vicat Softening Point | 165 °C | 329 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.13 @Frequency 1e+6 Hz |
3.13 @Frequency 1e+6 Hz |
ASTM D150 |
| 3.17 @Frequency 60 Hz |
3.17 @Frequency 60 Hz |
ASTM D150 | |
| Dielectric Strength | 19.3 kV/mm | 490 kV/in | ASTM D149 |
| Dissipation Factor | 0.00090 @Frequency 60 Hz |
0.00090 @Frequency 60 Hz |
ASTM D150 |